英国WA STELLOY C-S镍基超合金药芯焊丝
STELLOY C-S
EN 14700: TNi2
AWS A 5.21/ASME II C SFA 5.21: ERCNiCrMo-5A
DIN 85551: UP 23-GF-200/350-CKNTZ
1 Former classification replaced by EN 14700
• Nickel-based super-alloy flux-cored wire of the NiCrMoW type
• Particularly resistant to corrosion under oxidising and reducing atmospheres
• Weld metal is designed to withstand impact, compression, abrasion, oxidation, corrosion and heat up to 1100°C
• Excellent thermal shock resistance
• Can be machined without previous heat treatment
STELLOY C-S is suitable for welding of joints in steel clad with a nickel-chromium-molybdenum alloy and for the joining of nickel-chromium-molybdenum alloys to steel or to other nickel base alloys.
Base materials : UNS N 10002 ( ASTM B 334, B 336, B 366)
STELLOY C-S is also destined in general to surface all parts undergoing mechanical stress combined with corrosion, thermal shocks and/or high temperatures
Examples
Hot shear blades, lime kiln burner parts, dies, swages, press tools as well as pump parts, hot-piercing punches, rolling and wire-drawing guides, valves and reservoirs...
TYPICAL ALL-WELD METAL ANALYSIS with flux WAF 325
CMnSiCrMoFeWNi
|
0.05
|
0.60
|
0.50
|
16.00
|
16.00
|
5.00
|
4.50
|
Bal.
|
TYPICAL ALL-WELD METAL MECHANICAL PROPERTIES
Hardness:
|
As welded:
|
200HB
|
Work hardened:
|
350HB
WAF 325 - FLUX DESCRTPTION
|
Classification
|
EN 760: S A AB 1 65 DC H5
|
|
Basicity index
|
2.3 (according to Boniszewski)
|
|
Granulometry
|
0.25 - 2.5 mm
|
|
Current
|
DC by preference
|
|
Redrying
|
2 hours at 300 - 350°C
|
|
Packaging
|
bags (25 kg)
|
2.4
Other diameters: please consult us
Diameter < 2.4 mm > 2.4 mm
|
Standard packaging [EN ISO 544]
|
Spool : BS 300
|
Coil
|
Drum
|
|
Weight
|
15 kg
|
25 kg
|
Up to 330 kg
|
Other packaging: please consult us